Methods and apparatus for oxygen enriched flame-perforation of a polymer film

ABSTRACT

The present invention provides an apparatus and methods for flame-perforating polymeric films with an oxygen-enriched flame. One embodiment of the apparatus includes a frame, a support surface attached to the frame, where the support surface includes a plurality of lowered portions, an oxygen-enrichment system for increasing the amount of oxygen in the combustible mixture, a burner attached to the frame opposite the support surface, where the burner supports a stable flame, and a film contacting the support surface, where the flame of the burner is directed towards the film to cause the film to be perforated. One embodiment of the method of flame perforating a polymeric film includes igniting an oxygen-enriched combustible mixture to form a stable flame, wherein the flame generated by the oxygen-enriched combustible mixture provides more uniform perforations.

FIELD

The present invention relates to an apparatus and methods forflame-perforating films.

BACKGROUND

Various methods of making perforated polymer films are known. Forexample, U.S. Pat. No. 3,012,918 (Schaar), and British PatentSpecification Nos. GB 851,053 and GB 854,473 all generally describeprocesses and apparatuses for improving the heat-sealability ofpolymeric films by passing the film over a cooled, hollow, rotating,metal cylinder or support roll with a desired perforation pattern whilea jet of gas-heated air is directed onto the surface of the film so thatspecific areas of the film are melted, forming a pattern ofperforations.

U.S. Pat. No. 3,394,211 (MacDuff) discusses flame perforation ofheat-shrinkable, biaxially oriented polypropylene films. British PatentSpecification No. GB 1,012,963 and GB 1,073,605 disclose methods andapparatuses for flame perforating suitable thermoplastic films capableof being softened and melted by heat.

Oxygen-enriched flames have been used to improve the wettability oradhesion properties of polymer films. Such uses are disclosed in patentliterature that includes U.S. Pat. Nos. 3,153,683; 3,255,034; 3,347,697;3,361,607; 3,375,126; 3,431,135; 3,783,062; and 4,622,237 and 5,891,967.These patents describe the use of oxygen-enriched flames for the surfacemodification of polymers.

SUMMARY

One aspect of the present invention provides an apparatus forperforating a film with an oxygen-enriched flame. The apparatus forflame-perforating comprises: a frame; a support surface attached to theframe, where the support surface includes a plurality of loweredportions; a burner attached to the frame opposite the support surface,where the burner supports a flame; a burner pipe connected to theburner; an oxygen-enrichment system connected to the burner pipe,supplying an oxygen-enriched combustible mixture to the burner pipe; anda film contacting the support surface, wherein the flame of the burneris directed towards the film. In one embodiment of this apparatus amixer, connected to the burner pipe, facilitates the mixing ofappropriate volumes of oxygen, air and a gaseous hydrocarbon fuel toform the oxygen-enriched combustible mixture. In another embodiment ofthe above apparatus, the apparatus further includes a backing rollattached to the frame, where the backing roll includes the supportsurface, and where the film is wrapped around at least a portion of thesupport surface of the backing roll. In one aspect of this embodiment,the apparatus further includes a preheat roll attached to the frameadjacent the support surface, wherein the preheat roll includes an outersurface, and wherein the outer surface of the preheat roll is heated forpre-heating the film prior to the burner. In yet another aspect of thisembodiment, the outer surface of the preheat roll is heated greater than74° C. (165° F.) for pre-heating the film prior to the burner. In yetanother embodiment, the preheat roll is a nip roll attached to the frameadjacent the backing roll, wherein the film is between the nip roll andthe backing roll. In yet another aspect of this embodiment, the burneris positioned such that the angle measured between the burner and thenip roll is less than 45°, wherein a vertex of the angle is positionedat an axis of the backing roll.

In yet another embodiment, the apparatus further includes atemperature-controlled shield attached to the frame adjacent the backingroll, wherein the temperature-controlled shield is positioned betweenthe burner and the nip roll.

In another embodiment, the apparatus further includes an applicatorattached to the frame adjacent the support surface for applying eitherair or a liquid onto the support surface.

Another aspect of the present invention provides a method offlame-perforating film with an oxygen-enriched flame. The methodcomprises the steps of: providing a film having a first side and asecond side opposite the first side; contacting the second side of thefilm with a support surface having a plurality of lowered portions;contacting the first side of the film with a heated surface, removingthe heated surface from the first side of the film; enriching acombustible mixture with oxygen; igniting the combustible mixture toform a stable flame supported by a burner and fueled by theoxygen-enriched combustible mixture, and thereafter heating the firstside of the film with the flame from the burner to perforate the film.In one aspect of the above method, the perforating step perforates thefilm with a pattern corresponding to the plurality of lowered portionsof the support surface.

In one embodiment of the above method, the enriching step furthercomprises enriching an oxidizer with oxygen and combining theoxygen-enriched oxidizer with a gaseous hydrocarbon fuel to provide acombustible mixture. In another aspect of the above method, theoxygen-enriching step provides an oxidizer with an oxygen ratio greaterthan 0.21 and equal to or less than 0.35.

Another aspect of the present invention the method further comprisescooling the support surface to a temperature lower than 49° C. (120°F.). In another embodiment of the method, a preheated nip roll is usedfor contacting the first side of the film, wherein the nip roll isattached to the frame adjacent the backing roll, and wherein the film isbetween the nip roll and the backing roll.

In yet another embodiment of the above method, the burner is positionedsuch that the angle measured between the burner and the nip roll is lessthan 45°, wherein a vertex of the angle is positioned at an axis of thebacking roll.

In another embodiment of the method of flame-perforating film, themethod comprises the steps of: providing backing roll having a supportsurface, wherein the support surface includes a plurality of loweredportions; providing a nip roll, wherein the nip roll includes an outersurface, and wherein the outer surface of the nip roll is heated;enriching a combustible mixture with oxygen; igniting the combustiblemixture to form a stable flame supported by a burner and fueled by theoxygen-enriched combustible mixture, wherein the burner is positionedsuch that the angle measured between the burner and the nip roll is lessthan 45°, wherein the vertex of the angle is positioned at the axis ofthe backing roll; contacting a film against the support surface;pressing the film between the nip roll and the support surface of thebacking roll to pre-heat the film; and thereafter perforating the filmwith a flame of the burner.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will be further explained with reference to theappended Figures, wherein like structure is referred to by like numeralsthroughout the several views, and wherein:

FIG. 1 is a side view of a flame-perforating apparatus of the presentinvention;

FIG. 2 is a partial front view of the apparatus of FIG. 1 with two ofthe idler rolls and motor removed for clarity, and the backing rollshown in phantom lines;

FIG. 3 is a side view of the apparatus of FIG. 1 including film movingalong the film path within the apparatus;

FIG. 4 is a top plan view of a pattern of perforations in film, afterthe film has been perforated with the flame-perforating apparatus ofFIG. 1; and

FIG. 5 is a cross-sectional view of a tape including the film of FIG. 4.

DETAILED DESCRIPTION

The present invention provides embodiments of an apparatus forflame-perforating films and methods for flame-perforating films thatinclude an oxygen-enrichment system for the combustible mixture.Oxygen-enriched flames used for perforation assist in increasing the webspeed of the films being flame perforated while maintaining acceptablefilm quality. Acceptable film quality includes fully and uniformly open,consistently formed perforations in films without wrinkles or otherdefects, such as tears, thermal damage, or forming partially formedperforations. These qualities in a perforated elastomeric or polymericfilm are very important for particular end uses, such as providing anadhesive tape backing at a low cost with high tensile strength andexcellent conformability that has easy, straight, hand-tearability inboth the longitudinal and transverse direction, without unwantedelongation of the tape while hand-tearing.

The use of oxygen-enriched flames increases the speed of the perforationprocess and often improves the physical uniformity of the perforations.The perforation speed obtained using the present invention can be muchgreater than the speeds where oxygen enrichment is not employed.Additionally, significant improvement in perforation uniformity can alsobe attained.

Flames may be described in terms of two characteristics: the flame powerand the molar ratio of oxidizer to fuel. The flame power is the productof the volume of fuel burned per unit time and the heat content of thefuel. Typical units for the flame power are watts (W) or Btu/hr. Theflame power can be normalized to account for the dimensions of theburner, leading to units such as W/cm² or Btu/hr-in.

The exact ratio of oxidizer to fuel needed for complete combustion isknown as the stoichiometric ratio. For example, the exact amount of dryair necessary for the complete combustion of methane is 9.55 volumes ofdry air per volume of methane; so the stoichiometric ratio for anair:methane flame is 9.55:1 or alternatively expressed as just 9.55. Theequivalence ratio is defined as the stoichiometric oxidizer:fuel ratiodivided by the actual oxidizer:fuel ratio. For fuel-lean, or oxidizing,flames, there is more than the stoichiometric amount of oxidizer and sothe equivalence ratio is less than 1.00. For oxidizer:fuel mixtures atthe stoichiometric ratio, the equivalence ratio is equal to 1.00. Forfuel-rich systems, the equivalence ratio is greater than 1.00.

In the context of the present invention, oxygen enrichment involves theaddition of oxygen to the combustible mixture used to support thelaminar, premixed hydrocarbon flame that is used for perforating. Oxygenenrichment of the combustible mixture causes several changes to theflame, including an increased flame temperature, an increased laminarflame speed, and a decrease in the total flow of combustible mixturepassing through the burner. The increase in flame temperature occursbecause there is less inert nitrogen to be heated by the combustionreaction. The increase in flame speed causes the luminous flame conesthat are stabilized on the ribbon burner to decrease in size for a givenflame power. In other words, at a given flow rate of fuel, the height ofthe luminous flame cone will decrease as the concentration of oxygen inthe mixture increases at a constant equivalence ratio. The decrease inthe flow of combustible mixture is caused by the decreasing amount ofnitrogen in the oxidizer.

FIGS. 1 and 2 are illustrations of one embodiment of an apparatus formaking flame-perforated films of the present invention. FIG. 1illustrates a side view of the apparatus 10 and shows one embodiment ofoxygen-enrichment system 45. FIG. 2 illustrates a front view of aportion of apparatus 10, with the backing roll 14 shown in phantomlines, and with the idler rollers 55, 58 and motor 16 removed, forclarity.

The apparatus 10 includes a frame 12. The frame 12 includes an upperportion 12 a and a lower portion 12 b. The apparatus 10 includes abacking roll 14 having an outer support surface 15. The support surface15 preferably includes a pattern of lowered portions 90. These loweredportions 90 and the portions of the support surface 15 between thelowered portions collectively make up the support surface 15 of thebacking roll 14. The lowered portions 90 form a pattern of indentions inthe support surface 15. The lowered portions 90 may be a plurality ofdepressed or recessed portions or a plurality of indentations along thesupport surface 15. These lowered portions 90 are preferably etched intothe support surface 15. Alternatively, the pattern of lowered portions90 may be drilled, ablated, or engraved into the support surface 15. Thelowered portions 90 preferably are in the shape of ovals, and preferablyeach have an approximate length of 0.1778 cm (70 mils) or less, anapproximate width of 0.0762 mm (30 mils) or less, and an approximatedepth of 0.02032 cm (8 mils) or more. One example of a pattern ofperforations is taught in WO 02/11978, titled “Cloth-like PolymericFilms,” (Jackson et al.), that published on Feb. 14, 2002, which ishereby incorporated by reference for said pattern.

In one embodiment, the support surface 15 of the backing roll 14 istemperature-controlled, relative to the ambient temperature around theapparatus 10. The support surface 15 of the backing roll 14 may betemperature-controlled by any means known in the art. Preferably, thesupport surface 15 of the backing roll 14 is cooled by providing cooledwater into the inlet portion 56 a of hollow shaft 56, into the backingroll 14, and out of the outlet portion 56 b of the hollow shaft 56. Thebacking roll 14 rotates about its axis 13. The apparatus 10 includes amotor 16 attached to the lower portion 12 b of the frame. The motordrives a belt 18, which in turn rotates the shaft 56 attached to thebacking roll 14, thus driving the backing roll 14 about its axis 13.

The apparatus 10 includes a burner 36 and burner piping 38. Theapparatus 10 may include an optional exhaust hood (not shown) mountedabove the apparatus 10. The burner 36 and burner piping 38 are attachedto the upper portion 12 a of the frame 12 by burner supports 35. Theburner supports 35 may pivot about pivot points 37 by movement ofactuator 48 to move the burner 36 relative to the support surface 15 ofthe backing roll 14. The supports 35 may be pivoted by the actuator 48to position the burner 36 to a desired distance either adjacent or awayfrom the support surface 15 of backing roll 14. The combustible mixtureis fed to the burner 36 via burner pipes 38. Burner pipe 38 splits intoburner pipe 38 a and burner pipe 38 b, which connect to each end ofburner 36. Apparatus 10 includes an oxygen-enrichment system 45connected to opposite end of burner pipe 38, away from burner 36. Onecomponent of the oxygen enrichment system 45 is air line 41, whichconnects to burner pipe 38 via a venturi mixer 39. The flow of airthrough air line 41 is regulated by air flow controller 41 a. Oxygenline 43 is regulated by oxygen flow controller 43 a and feeds into airline 41 at oxygen inlet port 43 b. The oxygen enriched air flow iscarried to venturi mixer 39 via air line 41 to oxidizer inlet port 41 b.The fuel component of the combustible mixture is typically a gaseoushydrocarbon fuel and is regulated by fuel flow controller 47 a throughfuel line 47 into the venturi mixer 39 at fuel inlet port 47 b.Appropriate volumes of the gaseous fuel and oxygen-enriched air areregulated into the venturi mixer 39 to create a combustible mixture. Inone embodiment the fuel is natural gas.

The oxygen ratio is the ratio of the total flow of molecular oxygenpresent in the oxidizer to the total flow of all components in theoxidizer. The oxygen ratio in the oxidizer is calculated according tothe following expression, when the oxidizer consists of air and oxygen:Oxygen ratio=(F _(O2)+0.21F _(AIR))/(F _(O2) +F _(AIR))where F_(O2) is the flowrate of oxygen (in lpm or cfh) and F_(AIR) isthe flowrate of air (in lpm or cfh). It should be noted that the oxygenratio of air is approximately 0.21. An increase in the potential fordamage to the burner due to overheating and for hazardous flashback mayoccur as the oxygen ratio increases. Thus, most commercially availableribbon burners can only be safely operated at oxygen ratios below 0.35.Theoretically, a new burner design, which might include for example,modified burner port size and burner port distribution, as well asalternative burner ribbon and burner housing materials, could make itpossible to operate at higher oxygen ratios.

In one embodiment of the present invention, the apparatus 10 includes apreheat roll 20 attached to the lower portion 12 b of the frame 12. Thepreheat roll 20 includes an outer roll layer 22. The outer roll layer 22includes an outer surface 24. The outer roll layer may be made, forexample, of an elastomer, for example a high-service-temperatureelastomer. The preheat roll 20 may be, for example, a nip roll, whichmay be positioned against the backing roll 14 to nip the film betweenthe nip roll 20 and backing roll 14. However, it is not necessary thatthe preheat roll 20 be a nip roll and instead, the preheat roll may bepositioned away from the backing roll 14 so as to not contact thebacking roll 14. The nip roll 20 freely rotates about its shaft 60 andis mounted to roll supports 62. Linkage 46 is attached to roll supports62. The nip roll 20 may be positioned against the backing roll 14, usingactuator 44. When the actuator 44 is extended (as shown in FIG. 3), thelinkage 46 is rotated counterclockwise, and in turn, the roll supports62 are rotated counterclockwise until the nip roll 20 contacts thebacking roll 14. The actuator 44 may control the movement between thenip roll 20 and the backing roll 14, and thus may control the pressurebetween the nip roll 20 and backing roll 14. A stop 64 is attached tothe lower frame 12 b to inhibit the movement of the linkage 46 beyondthe lower frame 12 b, which limits the pressure applied by the nip roll20 against the backing roll 14.

In another embodiment of the present invention, the apparatus 10includes a temperature-controlled shield 26 attached to support 62 bybrackets 66 to form one assembly. Accordingly, when the actuator 44rotates the nip roll 20, as explained above, the shield 26 moves withthe nip roll. The shield 26 may be positioned relative to the nip roll20 by bolts 32 and slots 34 attached to the brackets 66. Thetemperature-controlled shield 26 may include a plurality of water-cooledpipes 28. However, other means of providing a temperature-controlledshield may be used, such as water-cooled plate, air-cooled plate, orother means in the art. The temperature-controlled shield 26 may bepositioned between the burner 36 and the nip roll 20. In this position,the shield 26 protects the nip roll 20 from some of the heat generatedfrom the burner 36, and thus, can be used to control the temperature ofthe outer surface 24 of the nip roll 20, which has the benefits ofreducing wrinkles or other defects in the film at the flame-perforationstep performed by the burner 36, while maintaining high film speeds.

In yet another embodiment of the present invention, the apparatus 10includes an optional applicator 50 attached to the lower portion 12 b offrame 12. The apparatus 10 includes a plurality of nozzles 52 connectedto applicator 50. In one embodiment, the applicator 50 is an airapplicator for applying air onto the backing roll 14. In anotherembodiment, the applicator 50 is a liquid applicator for applying liquidonto the backing roll 14. Preferably, the liquid is water, however otherliquids may be used instead. If the liquid is applied by the applicator50, then preferably, air is also supplied to the individual nozzles toatomize the liquid prior to application on the backing roll. The mannerin which the air or water may be applied to the backing roll 14 may bevaried by one skilled in the art, depending on the pressure, rate orvelocity of the air or water pumped through the nozzles 52. As explainedbelow, without wishing to be bound by any theory, it is believed that ifair or water is applied to the support surface 15 of the backing roll14, prior to contacting the film to the support surface 15, then thisapplication of air or water helps either remove some of the condensationbuilt up on the support surface 15 or applies additional water toactively control the amount of water between the film and the supportsurface, and thereby helps in eliminating wrinkles or other defectsformed in the film at the flame-perforation step conducted by the burner36.

The apparatus 10 includes a first idler roller 54, a second idler roller55, and a third idler roller 58 attached to the lower portion 12 b ofthe frame 12. Each idler roller 54, 55, 58 includes their own shafts andthe idler rollers may freely rotate about their shafts.

A variety of burners 36 are commercial available, for example, fromFlynn Burner Corporation, New Rochelle, N.Y.; Aerogen Company, Ltd.,Alton, United Kingdom, and Sherman Treaters Ltd., Thame, United Kingdom.A ribbon burner is typically desired for the flame perforation ofpolymer films, but other types of burners such as drilled-port or slotdesign burners may also be used. In one embodiment, the apparatus mayinclude a mixer (e.g. a venturi mixer) to combine the oxidizer and fuelbefore it feeds the flame used in the flame-perforating process of theinvention. In the embodiment represented by FIGS. 1 and 3, the oxygen isfirst introduced into the air stream, creating an oxygen-enrichedoxidizer stream. The oxygen-enriched oxidizer stream is then combinedwith the fuel stream in a venturi mixer to create an oxygen-enrichedcombustible mixture. However, the use of a mixer is not necessary andthe arrangement (order) of the air, oxygen and fuel lines may be inalmost any configuration, provided the final combustible mixture has anincreased amount of oxygen compared to air and provided the appropriatevolumes of fuel and oxidizer are combined prior to the burner to supporta uniform and stable flame.

FIG. 3 illustrates the path that the film travels through the apparatus10 and one preferred method of flame-perforating films. The film 70includes a first side 72 and a second side 74 opposite the first side72. The film travels into apparatus 10 and around first idle roller 54.From there, the motor-driven backing roll 14 pulls the film. In thisposition, the film is positioned between the nip roll 20 and the backingroll 14. In this step of the process, the second side 74 of the film 70is cooled by the water-chilled backing roll 14 and the first side 72 ofthe film 70 is simultaneously heated by the outer surface 24 of thepre-heat or nip roll 20. This step of preheating the film 70 with thenip roll outer surface 24 of the nip roll 20 prior to flame-perforatingthe film with the burner 36 unexpectedly provided the benefits ofreducing wrinkles or other defects in the perforated film.

The temperature of the outer support surface 15 of the backing roll 14may be controlled by the temperature of the water flowing through thebacking roll 14 through shaft 56. The temperature of the outer supportsurface 15 may vary depending on its proximity to the burner 36, whichgenerates a large amount of heat from the flames. In addition, thetemperature of the support surface 15 will depend on the material of thesupport surface 15.

The temperature of the outer surface 24 of the outer layer 22 of the niproll 20 is controlled by a number of factors. First, the flame power andthe temperature of the flames affect the temperature of outer surface 24of the nip roll 20. Second, the distance between the burner 36 and thenip roll 20 affects the temperature of the outer surface 24. Forexample, positioning the nip roll 20 closer to the burner 36 willincrease the temperature of the outer surface 24 of the nip roll 20.Conversely, positioning the nip roll farther away from the burner 36will decrease the temperature of the outer surface 24 of the nip roll20. The distance between the axis of nip roll 20 and the center of theburner face 40 of the burner 36, using the axis 13 of the backing roll14 as the vertex of the angle, is represented by angle α. Angle αrepresents the portion of the circumference of the backing roll or theportion of the arc of the backing roll between the nip roll 20 and theburner 36. It is preferred to make angle α as small as possible, withoutsubjecting the nip roll to such heat from the burner that the materialon the outer surface of the nip roll starts to degrade. For example,angle α is preferably less than or equal to 45°. Third, the temperatureof the outer surface 24 of the nip roll 20 may also be controlled byadjusting the location of the temperature-controlled shield 26 betweenthe nip roll 20 and the burner 36, using bolts 32 and slots 34 of thebrackets 66. Fourth, the nip roll 20 may have cooled water flowingthrough the nip roll, similar to the backing roll 14 described above. Inthis embodiment, the temperature of water flowing through the nip rollmay affect the surface temperature of the outer surface 24 of the niproll 20. Fifth, the surface temperature of the support surface 15 of thebacking roll 14 may affect the surface temperature of the outer surface24 of the nip roll 20. Lastly, the ambient temperature of the airsurrounding the nip roll 20 may also impact the temperature of the outersurface 24 of the nip roll 20.

The temperature of the support surface 15 of backing roll 14 may be inthe range of 7° C. to 54° C. (45° F. to 130° F.), in other embodimentsthis temperature may be in the range of 10° C. to 41° C. (50° F. to 105°F.). The temperature of the nip roll surface 24 of nip roll 20 may be inthe range of 74° C. to 204° C. (165° F. to 400° F.), in otherembodiments this temperature may be in the range of 82° C. to 121° C.(180° F. to 250° F.). However, the nip roll surface 24 should not riseabove the temperature at which the nip roll surface material may startto melt or degrade. Although the temperature of the support surface 15of the backing roll 14 and the temperature of the nip roll surface 24 ofthe nip roll 20 are listed above, one skilled in the art, based on thebenefits of the teaching of this application, could select temperaturesof the support surface 15 and nip roll surface 24 depending on the filmmaterial and the rotational speed of the backing roll 14 toflame-perforate film with reduced numbers of wrinkles or defects.

Returning to the process step, at this location between the preheat roll20 and backing roll 14, the preheat roll preheats the first side 72 ofthe film 70 prior to contacting the film with the flame of the burner.Unexpectedly, the temperature of the preheat roll is critical in helpingto eliminate wrinkles or other defects in the film at theflame-perforation step.

In the next step of the process, the backing roll 14 continues to rotatemoving the film 70 between the burner 36 and the backing roll 14. Thisparticular step is illustrated in FIG. 3. When the film comes in contactwith the flames of the burner 36, the portions of the film that aredirectly supported by the chilled metal support surface are notperforated because the heat of the flame passes through the filmmaterial and is immediately conducted away from the film by the coldmetal of the backing roll 14, due to the excellent heat conductivity ofthe metal. However, a pocket of air is trapped behind those portions ofthe film material that are covering the etched indentations or loweredportions 90 of the chilled support material. The heat conductivity ofthe air trapped in the indentation is much less than that of thesurrounding metal and consequently the heat is not conducted away fromthe film. The portions of film that lie over the indentations then meltand are perforated. As a result, the perforations formed in the film 70correlate generally to the shape of the lowered portions 90. At aboutthe same time that film material is melted in the areas of the loweredportions 90, a raised ridge or edge 120 (shown only in FIGS. 4 and 5) isformed around each perforation, which consists of the film material fromthe interior of the perforation that has contracted upon heating.

After the burner 36 has flame-perforated the film, the backing roll 14continues to rotate, until the film 70 is eventually pulled away fromthe support surface 15 of the backing roll 14 by the idler roller 55.From there, the flame-perforated film 70 is pulled around idler roll 58by another driven roller (not shown). The flame-perforated film may beproduced by the apparatus 10 in long, wide webs that can be wound up asrolls for convenient storage and shipment. Alternatively, the film 70may be combined with a layer of pressure-sensitive adhesive or otherfilms to provide tape, as discussed in reference to FIG. 5.

As mentioned above, the apparatus 10 may include the optional applicator50 for either applying air or water to the support surface 15 of thebacking roll 14, prior to the film 70 contacting the support surfacebetween the backing roll 14 and the nip roll 20. Without wishing to bebound by any theory, it is believed that controlling the amount of waterbetween the film 70 and the support surface 15 helps reduce the amountof wrinkles or other defects in the flame-perforated film. There are twoways in which to control the amount of water between the film 70 and thesupport surface 15. First, if the applicator 50 blows air onto thesupport surface, then this action helps reduce the amount of water buildup between the film 70 and support surface 15. The water build up is aresult of the condensation that is formed on the backing roll surfacewhen the water-cooled support surface 15 is in contact with thesurrounding environment. Second, the applicator 50 may apply water orsome other liquid to the support surface 15 to increase the amount ofliquid between the film 70 and the support surface. Either way, it isbelieved that some amount of liquid between the film 70 and the supportsurface 15 may help increase the traction between the film 70 and thesupport surface 15, which in turn helps reduce the amount of wrinkles orother defects in the flame-perforated film. The position of the nozzles52 of the applicator 50 relative to the centerline of the burner 36 isrepresented by angle β, where the vertex of the angle is at the axis 13of the backing roll 14. In one embodiment, the applicator 50 is at anangle β greater than angle α, so that the air or water is applied to thebacking roll 14 prior to the nip roll 20.

The burner supports 35 and the actuator 48, as explained above inreference to FIG. 1, may adjust the relative distance between the burner36 and backing roll 14. The flame is a luminous cone supported by theburner, the height of which can be measured with means known in the art,from burner housing face to the tip of the flame. Actually, the ribbonburner 36 has a plurality of flames and preferably, all flame tips areat the same position relative to the burner housing, preferably uniformin length. However, the flame tips could vary, for example, depending onnon-uniform ribbon configurations or non-uniform gas flow into theribbons. For simplicity, the plurality of flames is referred to as oneflame. The distance between the face 40 of the burner 36 and the firstside 72 of the film 70 is referred to as the burner-to-film separationdistance.

Preferably, the film 70 a polymeric substrate. The polymeric substratemay be of any shape that permits perforation by flame and include, forexample, films, sheets, porous materials and foams. Such polymericsubstrates include, for example, polyolefins, such as polyethylene,polypropylene, polybutylene, polymethylpentene; mixtures of polyolefinpolymers and copolymers of olefins; polyolefin copolymers containingolefin segments such as poly(ethylene vinylacetate), poly(ethylenemethacrylate) and poly(ethylene acrylic acid); polyesters, such aspoly(ethylene terephthalate), poly(butylene phthalate) and poly(ethylenenaphthalate); polystyrenes; vinylics such as poly(vinyl chloride),poly(vinylidene dichloride), poly(vinyl alcohol) and poly(vinylbutyral); ether oxide polymers such as poly(ethylene oxide) andpoly(methylene oxide); ketone polymers such as polyetheretherketone;polyimides; mixtures thereof, or copolymers thereof. Preferably, thefilm is made of oriented polymers and more preferably, the film is madeof biaxially oriented polymers. Biaxially oriented polypropylene (BOPP)is commercially available from several suppliers including: ExxonMobilChemical Company of Houston, Tex.; Continental Polymers of Swindon, UK;Kaisers International Corporation of Taipei City, Taiwan and PT IndopolySwakarsa Industry (ISI) of Jakarta, Indonesia. Other examples ofsuitable film material are taught in WO 02/11978, titled “Cloth-likePolymeric Films,” (Jackson et al.).

FIG. 4 illustrates a top view of a pattern of perforations in film afterit has been perforated with the flame-perforating apparatus of FIG. 1.The perforations are typically elongate ovals, rectangles, or othernon-circular or circular shapes arranged in a fashion such that themajor axis of each perforation intersects adjacent perforations orpasses near adjacent perforations. As shown in FIG. 5, this perforatedpolymeric film 114 can be joined to one or more additional layers orfilms, such as a top layer to provide durability or impermeability, or abottom layer to provide adhesiveness.

The perforation pattern formed in polymeric film 114 has a stronginfluence on the tear and tensile properties of the perforated films andtape backings of the invention. In FIG. 4, a portion of an enlargedlayout of a typical perforation pattern 128 is shown, with the machinedirection oriented up and down, and the transverse direction orientedleft to right. Depicted perforation pattern 128 comprises a series ofrows of perforations, identified as a first row having perforations 1 a,1 b, and 1 c; a second row having perforations 2 a, 2 b, and 2 c; athird row having perforations 3 a, 3 b, and 3 c; a fourth row havingperforations 4 a, 4 b, and 4 c; and a fifth row having perorations 5 a,5 b, and 5 c. The perforation pattern 128 includes other rows ofperforations, similar to the first row through the fifth row. Eachperforation includes a raised ridge or edge 120. In specificimplementations, this raised ridge 120 has been observed to provideenhanced tear properties of the perforated film 114. The raised ridge120 can also impart slight textures that cause the film 114 to moreclosely resemble a cloth-like material. Typically the perforations forma pattern extending along most or all of the surface of a film, and thusthe pattern shown in FIG. 4 is just a portion of one such pattern.

As explained above in reference to FIG. 4, the perforation pattern 128formed in film 114 correlates generally to the pattern of loweredportions 90 formed into the support surface 15 of backing roll 14. Thefilm shown in FIG. 4 includes numerous perforations, each of which aregenerally oval-shaped, preferably includes a length of approximatelythree-times greater than the width. However, one skilled in the artcould select any pattern of lowered portions 90 in support surface 15 ofthe backing roll 14 to create alternative perforation patterns or sizes.

The films described herein are suited for many adhesive tape backingapplications. The presence of a top film over the perforation patterncan provide an appearance similar to a poly-coated cloth-based tapebacking in certain embodiments. This appearance, combined with thetensile and tear properties, makes the film useful as a backing for ducttape, gaffer's tape, or the like. Particularly for duct tape,incorporation of known appropriate pigments for a silver-gray colorationinto the top film contributes to a familiar appearance, which is desiredin the marketplace. Because the backing is conformable, it is alsouseful as a masking tape backing.

FIG. 5 illustrates a cross-sectional view of one embodiment of a tape112 including the film of FIG. 4 as a tape backing. Tape 112 contains aperforated film 114 having first major surface 116 and second majorsurface 118. Perforated film 114 contains perforations 115 extendingthrough its thickness. In the embodiment illustrated, the edges of eachperforation 115 along second major surface 118 include raised portions120. Perforated film 114 is typically an oriented film, e.g. a biaxiallyoriented film.

Polymeric tape 112 further includes a top film 122 and a bottom layer124. In the embodiment illustrated, top film 122 provides durability tothe polymeric tape 112, and can further increase the strength and impartfluid impermeability to tape 112. Bottom layer 124 is, for example, anadhesive composition. Additional or alternative layers can be used tocreate tape 112. The arrangement of the layers can also be changed.Thus, for example, the adhesive can be applied directly to the top film122 rather than to the perforated layer.

The operation of the present invention will be further described withregard to the following detailed examples. These examples are offered tofurther illustrate the various specific and preferred embodiments andtechniques. It should be understood, however, that many variations andmodifications may be made while remaining within the scope of thepresent invention.

EXAMPLES

A custom-designed flame perforation system described in U.S. patentapplication Ser. No. 10/267,538 was modified by adding anoxygen-enrichment system. Flow-control hardware was used to enable theinjection of oxygen into the air stream, forming an oxidizer streamimmediately prior to the venturi mixer where the oxidizer stream andnatural gas fuel were combined to form a combustible mixture. The flowof ultra-high-purity oxygen (>99.99%), available from Oxygen Service Co.of St. Paul Minn., at a gage pressure of 276 kPa (40 psi) was measuredusing a Millipore Tylan FC-2921V-J mass flow controller. The oxygenratio in the oxidizer stream was calculated as described above.

Examples of perforated films of biaxially oriented polypropylene (BOPP)were produced under the following operating conditions. Dust-filtered,25° C. compressed air was injected with oxygen as stated above and thenmixed with a natural gas fuel (having a specific gravity of 0.577, astoichiometric ratio of dry air to natural gas of 9.6:1, and a heatcontent of 37.7 kJ/L) in a venturi mixer, available from Flynn BurnerCorporation, of New Rochelle, N.Y., to form a combustible mixture. Theflow rates of natural gas and air were controlled with control valvesavailable from Foxboro-Eckardt GmbH of Stuttgart, Germany, and weremeasured with mass flow meters available from Flow Technology Inc. ofPhoenix, Ariz. All flows were adjusted to result in a flame equivalenceratio of 0.96 and a normalized flame power of 1600 W/cm² (15,000Btu/hr-in.). The combustible mixture passed through a 3 meter long pipeto a ribbon burner, which consisted of a 33 cm×1 cm, 6-port corrugatedstainless steel ribbon mounted in a brass housing, Series 850, suppliedby Flynn Burner Corporation, New Rochelle, N.Y.

The burner was mounted adjacent a 35.5 cm diameter, 46 cm face-width,steel, double-shelled, spirally-wound, chilled backing roll, availablefrom F.R. Gross Company, Inc., Stow Ohio. The temperature of the backingroll was controlled by a 227 l/min (60 gal/min) recirculating flow ofwater at a temperature of 7.2° C. (45° F.). The steel backing roll shellwas plated with 0.5 mm of copper of a 220 Vickers hardness, thenengraved by Custom Etch Rolls Inc. of New Castle, Pa., with aperforation pattern shown in FIG. 6 of U.S. patent application Ser. No.10/267,538. Filtered, compressed air at a pressure of 69 kPa/m² (10 psi)was directed onto the chilled backing roll to controllably reduce theamount of water condensation accumulating on the patterned portion ofthe backing roll.

An electric spark ignited the combustible mixture. Stable conical flameswere formed with tips at a distance of approximately 9-20 mm from theface of the burner housing. For oxygen ratios of 0.21, 0.23, 0.25 and0.27, the size of the flame cones were approximately 20 mm, 16 mm, 12mm, and 9 mm, respectively. The distance between the ribbons 42 and theface 40 of the burner 36 was equal to 3 mm. A thermally extruded,biaxially oriented polypropylene (BOPP) homopolymer film, which was 0.03mm (1.2 mil) thick and 30 cm wide, was guided by idler rolls to wraparound the chilled backing roll and processed through the system at anadjustable speed. The film web was maintained at an upstream anddownstream tension of approximately 1.5 N/lineal cm (0.8 lbs/linealinch).

To ensure intimate contact between the BOPP film and the chilled backingroll, a 10 cm diameter, 40 cm face-width, inbound nip roll, availablefrom American Roller Company, Kansasville, Wis., covered with 6 mm of VN110 (80 Shore A durometer) VITON fluoroelastomer, was located at aposition of approximately 45 degrees relative to the burner, on theinbound side of the chilled backing roll. Positioned between the niproll and the burner, a water-cooled shield was maintained at atemperature of 50° F. (10° C.) with recirculating water. The niproll-to-backing roll contact pressure was maintained at approximately 50N/lineal cm.

Table 1 shows the results of an experiment where the burner-to-filmdistance (the distance between the surface of the burner face 40 housingand the first side 72 of the film 70) was varied between 5 to 14 mmwhile the oxygen ratio in the oxydizer stream was maintained at either0.21, 0.23, 0.25 or 0.27, where the oxygen ratio of 0.21 is essentiallyair with no oxygen enrichment. For example, a maximum web speed of 95m/min was achieved while maintaining acceptable hole size under theprocess conditions of burner-to-film separation of 5 mm and 0.27 oxygenratio. Given that the size of the flame cone was approximately 9 mmbeyond the burner, the flame impinged the film by approximately 4 mm.

Using an Olympus SZH-1LLD optical microscope with a 100× eyepiece, thedimensions of the perforations (holes) generated in the BOPP films weremeasured. As shown in FIG. 6 of U.S. patent application Ser. No.10/267,538, the perforated holes were in the shape of an ellipse or ovalhaving both a major and a minor axis. Both axes were measured on atleast 50 randomly chosen holes or, alternately, on sufficient numbers ofrandomly chosen holes to generate a normal distribution of measurementdata if 50 measurements had not already defined a normal distribution.The maximum number of holes that needed to be measured to generate thenormal distribution was 75. A normal distribution of hole-dimensionmeasurements was desirable so that the data could be better analyzedstatistically to quantify the perforation quality.

For each combination of process conditions (burner-to-film separationand oxygen ratio), the maximum film speed was determined that stillenabled 100% open perforations across the entire width of the 30-cm BOPPfilm. Perforations at each process condition were required to haveapproximately the same average major axis dimension of 0.813 mm (32.0mil). By maintaining the same size perforation at all of the processconditions investigated, more consistent speed and quality comparisonswere made.

Thus, to evaluate the effect of an oxygen-enriched flame on perforationquality, the maximum speed in meters/min that continued to provide 100%open perforations across the entire width of the film was determined foreach oxygen ratio level and burner-to-film separation distance. In otherwords, through the statistical measurement means described above, theperforation hole size was held constant, while the process conditions ofoxygen ratio and burner-to-film separation were varied to determine themaximum process speed. In most cases the perforation uniformity has alsobeen improved as compared with a flame perforation process using nooxygen-enrichment. TABLE 1 Maximum Perforation Speed (m/min) 0.23 O₂0.25 O₂ 0.27 O₂ Burner-to-film 0.21 O₂ oxygen- oxygen- oxygen-Separation (mm) nominal air enriched enriched enriched 5 53 83 93 95 650 75 80 85 7 52 63 72 80 8 50 55 61 68 9 50 57 60 65 10 45 53 53 60 1145 50 55 65 12 40 42 47 56 13 38 41 44 49 14 36 39 41 48

Foreseeable modifications and alterations of this invention will beapparent to those skilled in the art without departing from the scopeand spirit of this invention. This invention should not be restricted tothe embodiments that are set forth in this application for illustrativepurposes.

1. An apparatus for flame-perforating film, comprising: a frame; asupport surface attached to the frame, wherein the support surfaceincludes a plurality of lowered portions; a burner attached to the frameopposite the support surface, wherein the burner supports a flame; aburner pipe connected to the burner; and an oxygen-enrichment systemconnected to the burner pipe.
 2. The apparatus of claim 1, comprising afilm contacting the support surface, wherein the flame of the burner isdirected towards the film.
 3. The apparatus of claim 2, furthercomprising a backing roll attached to the frame, wherein the backingroll includes the support surface, and wherein the film is wrappedaround at least a portion of the support surface of the backing roll. 4.The apparatus of claim 2, further including a preheat roll attached tothe frame adjacent the support surface, wherein the preheat rollincludes an outer surface, and wherein the outer surface of the preheatroll is heated for pre-heating the film prior to the burner.
 5. Theapparatus of claim 4, wherein the outer surface of the preheat roll isheated greater than 74° C. (165° F.) for pre-heating the film prior tothe burner.
 6. The apparatus of claim 4, wherein the preheat roll is anip roll attached to the frame adjacent the backing roll, wherein thefilm is between the nip roll and the backing roll.
 7. The apparatus ofclaim 6, further including a temperature-controlled shield attached tothe frame adjacent the backing roll, wherein the temperature-controlledshield is positioned between the burner and the nip roll.
 8. The methodof claim 6, wherein the burner is positioned such that the anglemeasured between the burner and the nip roll is less than 45°, wherein avertex of the angle is positioned at an axis of the backing roll.
 9. Theapparatus of claim 1, further comprising a mixer, connected to theburner pipe, wherein the mixer facilitates the mixing of appropriatevolumes of oxygen, air and a gaseous hydrocarbon fuel to form theoxygen-enriched combustible mixture.
 10. The apparatus of claim 1,further including an air applicator attached to the frame adjacent thesupport surface for blowing air onto the support surface.
 11. Theapparatus of claim 1, further including a liquid applicator attached tothe frame for applying liquid onto the support surface.
 12. A method offlame-perforating film, comprising the steps of: providing a film havinga first side and a second side opposite the first side; contacting thesecond side of the film with a support surface having a plurality oflowered portions; contacting the first side of the film with a heatedsurface; removing the heated surface from the first side of the film;enriching a combustible mixture with oxygen; igniting the combustiblemixture to form a stable flame supported by a burner and fueled by theoxygen-enriched combustible mixture; and thereafter heating the firstside of the film with the flame from the burner to perforate the film.13. The method of claim 12, wherein the enriching step further comprisesenriching an oxidizer with oxygen and combining the oxygen-enrichedoxidizer with a gaseous hydrocarbon fuel to provide a combustiblemixture.
 14. The method of claim 13, wherein the oxygen-enriching stepprovides an oxidizer with an oxygen ratio greater than 0.21.
 15. Themethod of claim 13, wherein the oxygen-enriching step provides anoxidizer with an oxygen ratio greater than 0.21 and equal to or lessthan 0.35.
 16. The method of claim 12, wherein the perforating stepperforates the film with a pattern corresponding to the plurality oflowered portions of the support surface.
 17. The method of claim 12,further comprising cooling the support surface to a temperature lowerthan 49° C. (120° F.).
 18. The method of claim 17, wherein the coolingstep includes cooling the support surface to a temperature lower than41° C. (105° F.) to cool the second side of the film.
 19. The method ofclaim 12, wherein the heated surface is greater than 74° C. (165° F.);20. The method of claim 12, wherein a preheated nip roll is used forcontacting the first side of the film, wherein the nip roll is attachedto the frame adjacent the backing roll, and wherein the film is betweenthe nip roll and the backing roll.
 21. The method of claim 20, furthercomprising positioning the burner such that the angle measured betweenthe burner and the nip roll is less than 45°, wherein a vertex of theangle is positioned at an axis of the backing roll
 22. A method offlame-perforating film, comprising the steps of: providing backing rollhaving a support surface, wherein the support surface includes aplurality of lowered portions; providing a nip roll, wherein the niproll includes an outer surface, and wherein the outer surface of the niproll is heated; enriching a combustible mixture with oxygen; ignitingthe combustible mixture to form a stable flame supported by a burner andfueled by the oxygen-enriched combustible mixture, wherein the burner ispositioned such that the angle measured between the burner and the niproll is less than 45°, wherein a vertex of the angle is positioned at anaxis of the backing roll; contacting a film against the support surface;pressing the film between the nip roll and the support surface of thebacking roll to pre-heat the film; and thereafter perforating the filmwith a flame of the burner.
 23. The method of claim 22, wherein theenriching step further comprises enriching an oxidizer with oxygen andcombining the oxygen-enriched oxidizer with a gaseous hydrocarbon fuelto create a combustible mixture.
 24. The method of claim 23, wherein theoxygen-enriching step provides an oxidizer with an oxygen ratio greaterthan 0.21.
 25. The method of claim 24, wherein the oxygen-enriching stepprovides an oxidizer with an oxygen ratio greater than 0.21 and equal toor less than 0.35.
 26. The method of claim 22, wherein the perforatingstep perforates the film with a pattern corresponding to the pluralityof lowered portions of the support surface
 27. The method of claim 22,further comprising providing a temperature-controlled shield, whereinthe temperature-controlled shield is positioned between the burner andthe nip roll.
 28. The method of claim 22, further comprising cooling thesupport surface to a temperature lower than 49° C. (120° F.);
 29. Themethod of claim 28, wherein the cooling step including cooling thesupport surface to a temperature lower than 41° C. (105° F.) to cool thesecond side of the film.